Nylon

PAHT K7CFLM 500gr

Quantity: 500g
Empty weight coil: 250g
Diameter of the spool: ca.20cm - Width: ca.6,5cm - Inner diameter hub: ca.5,5cm

Total: 800g

Density in g/cm3: 1,03
Diameter: 1,75mm +/- 0,04mm
Roundness: +/-3

Carbon: 15%

Pressure temperature: 270-290 °C
Bed temperature: 70-100 °C

PAHT K7CFLM is a PA12-based carbon fiber reinforced nylon material with low water absorption and a significant increase in strength, stiffness and heat deflection temperature. This high-performance material can be printed using a commercial printer with a heating platform. It is suitable for lightweight parts that are oil and wear resistant or require high strength. It is recommended to use printing nozzles with diameter over 0.6 mm made of wear resistant materials.
High mechanical performance High strength and stiffness Carbon fiber reinforced.

We recommend the use of hardened steel or ruby nozzles with a diameter of 0.5 mm or 0.6 mm.

Properties

Reinforced with carbon fiber
High tensile strength
High stiffness
Dimensional stability
High thermal resistance
High chemical resistance
Low shrinkage and distortion = excellent dimensional stability
Possibility to print with an open printer

To compensate for unevenness on the print bed, the first layer should be printed with a thickness of 0.3mm. The fan should be set to 0 if possible.
A closed installation space and good ventilation is recommended!